Materials & Technology 112 - Coursework Example
Summary
A network Bakelite has a greater tensile strength than a lightly cross-linked polyethylene.1 Crosslinking hinder the re-organization of molecules during crystallization; hence, a lightly cross-linked polyethylene has a lower degree of crystallinity as compared to its linear… 
- Subject: Miscellaneous
- Type: Coursework
- Level: Ph.D.
- Pages: 2 (500 words)
- Downloads: 0
- Author: alyssonschultz
Save Your Time for More Important Things
Let us write or edit the coursework on your topic
"Materials & Technology 112"
with a personal 20% discount.
GRAB THE BEST PAPER
Extract of sample
Materials & Technology 112
Download file to see previous pages...
Crystallization markedly enhances strength, rigidity, and opacity of a polymer. High density polyethylene, then, is the stiffest of all types of polyethylene due to its high degree of crystallinity. Thereby, high density polyethylene has a greater tensile strength than low density polyethylene.
Branching tend to impede crystallization, making a polymer less rigid, more easily to deform, and weaker4. Thus, a 95% crystalline and linear polytetrafluoroethylene (PTFE) has a greater tensile strength than a 95% crystalline and branched PTFE.
Molecular weight data for some polymer are tabulated below. Compute (a) the number-average molecular weight, and (b) the weight-average molecular weight. (c) If it is known that this material’s degree of polymerisation is 477, which one of the polymers listed in Table 14.3 of the lecture notes is this polymer? Why?
Carbon dioxide diffuses through a high density polyethylene (HDPE) sheet 50 mm thick at a rate of 2.2 10-8 (cm3 STP)/cm2-s at 325 K. The pressures of carbon dioxide at the two faces are 4000 kPa and 2500 kPa, which are maintained constant. Assuming conditions of steady state, what is the permeability coefficient at 325 ...Download file to see next pagesRead More
Branching tend to impede crystallization, making a polymer less rigid, more easily to deform, and weaker4. Thus, a 95% crystalline and linear polytetrafluoroethylene (PTFE) has a greater tensile strength than a 95% crystalline and branched PTFE.
Molecular weight data for some polymer are tabulated below. Compute (a) the number-average molecular weight, and (b) the weight-average molecular weight. (c) If it is known that this material’s degree of polymerisation is 477, which one of the polymers listed in Table 14.3 of the lecture notes is this polymer? Why?
Carbon dioxide diffuses through a high density polyethylene (HDPE) sheet 50 mm thick at a rate of 2.2 10-8 (cm3 STP)/cm2-s at 325 K. The pressures of carbon dioxide at the two faces are 4000 kPa and 2500 kPa, which are maintained constant. Assuming conditions of steady state, what is the permeability coefficient at 325 ...Download file to see next pagesRead More